Printing here with eSun PLA at 215 C on a Prusa Mini, and there are lots of hairline strings.
What’s causing those strings? Temp too low?
You must log in or register to comment.
Often a combination of temp too high, not enough retraction, or water contaminated filament.
If the plastic in the hot end is too hot it will keep “running” out of the nozzle after retraction and you’ll get strings. Similarly if you don’t retract enough to actually pull plastic out of the nozzle during a rapid move, it will want to keep pushing thru. This is supported by the little blobs it leaves on that angled surface corner its travelling to when stringing, thats excess material squeezing out during its rapid moves then being left on that wall.
And if there’s water in your filament all bets are off on how it’ll behave.215 is pretty warm for that esun PLA especially if you’re using the stock brass nozzle, try bumping that down to 205 or even 200, and increase your retraction speed and distance settings in prusaslicer a tiny amount (0.1mm distance, 2mm/s speed at a time until you see improvement is plenty)
Use a temperature calibration tower to test things out.
This guy 3Dprints.
What a treat of a post. This is why I subscribe to !3dprinting@lemmy.world. Thank you.
Hell yeah I do. I help run the makerspace at my college. I’ve fixed damn near every problem a Prusa can have at this point lol
Thank you! <3 The print finished and now I am running a temp tower to check what works better than what I had. I would then work on adjusting the retraction, too. Also, this filament is straight out of the factory wrap so it should be dry enough.
Glad to help, and good luck! This is only the first step into becoming a master print tuner.
Great advice
Something else that contributes to stringing is using Z-hop as there’s nothing to wipe the nozzle clean. My printer is calibrated well and I still get stringing when using Z-hop.
Yeah z hop should really be close to off unless you have a really really narrow print profile.
Based on the layers of his print I’d say he also needs to level his bed
I guess you refer to the right part of the base, right? What you’re seeing is actually a sort of staircase with shadows, because that right-hand part of the print is angled a few degrees up. So it only looks bad in this lighting, but it’s fine.
See the left side of the base, that’s really flat and is fine.
Well I was saying it because the first layer looks very thin and the appears to be some parts on the infill on the left side that look like the nozzle rubbed the print
Hmm, interesting, thanks. The Prusa Mini has auto bed leveling so it’s not that, but maybe I need to adjust the Z offset generally.
It’s very hard for me to tell, even when wearing my good glasses…! So tiny… I did a Z test just the other day that looked and felt smooth, not too deep and not too high, gotta try again.
I could be wrong, I’d def look up what different print issues look like before taking my word from a single picture lol
Try dehydrateding your pla first. Then try some of these other suggestions. If all else fails, these clean up really nicely with a butane blow torch.
You already got a good answer about lowering temp and tuning retraction. Other than that, you have underextrusion there (gaps in the flat part on the build plate). I think you should extend your calibration:
Calibrate temp - flow - retraction
To reduce stringing you want:
- lower temp
- higher retraction
- faster travel speed
Be careful with first two, if you go too far you might get a clog. Sometimes its just better to accept some stringing, but since you are at 215 I bet it can be improved quite easy
I can’t add anything concerning stringing that the other comment didn’t already cover, so I’ll ask about the gaps.
Have you tried upping the flow rate to fill them in? The other option I’ve used in the past was lowering my Z Offset if the flow was alright.
Keep in mind that changing your flow rate will likely also cause you have to mess with your retraction settings again.
Haven’t printed too much, so take my comment with a grain of salt. But I don’t think the temperature is the problem. I notice that I get strings when I set my slicer to not do retraction. I guess that makes sense intuitively - strings are just plastic where they shouldn’t be, and the best way to prevent that is to make sure to retract the plastic away from the print.
Also, I think 215 is slightly high, or at least higher than what I use